Heat resistance high alumina cement 80 introduction
As a high purity product, heat resistance high alumina cement CA80 contains approximately 80% alumina, and Kerui 80% high alumina cement is represented by two product types, CA80 and CA80S.
![Refractory Cement CA80](https://www.krbrick.com/wp-content/uploads/2021/01/2021022607550684.jpg)
![Refractory Cement CA80](https://www.krbrick.com/wp-content/uploads/2021/01/2021022607550564.jpg)
![Refractory Cement CA80](https://www.krbrick.com/wp-content/uploads/2021/01/202102260755064.jpg)
Heat resistance high alumina cement 80 feature
- Anti-freezing
- High purity
- For emergency maintenance
- Rapid hardening and early strengthening
- Stable corrosion resistance of surface effects
Notes: refractory cement = high alumina cement = Calcium aluminate cement
More relevant refractory products: Corundum Mullite Fire Bricks
Heat resistance high alumina cement 80 index
Products | CA75 | CA75 | CA80 | CA80 | CA80S | CA80S |
Workable time | Moderate | Moderate | Short | Short | Longer | Longer |
Standard | Usual range | Specification limit | Usual range | Specification limit | Usual range | Specification limit |
SiO2, % | 0.1-0.4 | ≤0.5 | 0.1-0.4 | ≤0.5 | 0.1-0.4 | ≤0.5 |
Al2O3, % | 73.5-75.5 | ≥73 | 78.0-80.0 | ≥77 | 78.0-80.0 | ≥77 |
Fe2O3, % | 0.1-0.4 | ≤0.5 | 0.1-0.4 | ≤0.5 | 0.1-0.4 | ≤0.5 |
CaO, % | 21.0-23.0 | – | 18.5-20.5 | – | 18.5-20.5 | – |
R2O, % | – | ≤0.4 | – | ≤0.4 | – | ≤0.4 |
S-, % | – | ≤0.1 | – | ≤0.1 | – | ≤0.1 |
CI-, % | – | ≤0.06 | – | ≤0.06 | – | ≤0.06 |
d50(μm) | 6-9 | ≤10 | 5-8 | ≤9 | 5-8 | ≤9 |
325M(%) | – | ≤5.0 | – | ≤5.0 | – | ≤5.0 |
Specific surface areas(㎡/kg) | 420-480 | ≥400 | 450-500 | ≥450 | 450-500 | ≥450 |
Setting time, min | ||||||
Initial setting time IS | 150-200 | ≥150 | 150-210 | ≥30 | 210-270 | ≥180 |
Final setting time FS | 240-300 | ≤360 | 210-270 | ≤300 | 260-320 | ≤360 |
Flexural strength, Mpa | ||||||
1d | 6.5-8.5 | ≥4.0 | 6.0-8.0 | ≥4.0 | 5.5-7.5 | ≥4.0 |
3d | 8.5-10.5 | ≥5.0 | 7.0-9.0 | ≥5.0 | 7.0-9.0 | ≥5.0 |
Compressive strength, Mpa | ||||||
1d | 42-52 | ≥25 | 40-50 | ≥25 | 35-45 | ≥25 |
3d | 52-62 | ≥30 | 50-60 | ≥30 | 50-60 | ≥30 |
Heat resistance high alumina cement 80 application
The special properties of high alumina cement CA80 give high performance concrete the following characteristics: high fire resistance and excellent mechanical properties.
Heat resistance high alumina cement 80 can be used for conventional and low-cement castables in the refractory industry, where rapid setting, high early strength development and good medium-temperature strength are required. The high purity of CA80 makes it suitable for certain refractory applications. For example, low silica and iron oxide are essential in reducing atmospheres where hydrogen or carbon monoxide is present.
【Additional Information】
Principal phase: CA, CA2, Aα
Secondary phase: C12A7
Pyrometric cone equivalent: 1750-1800℃
Bulk density: 800-900 kg/m3
Specific gravity: 3.1-3.2 g/cm3
Shelf Life: 6 months
【Packaging and Storage】
Packing method: Standard export packaging
Paper bags: 25/50kg
Big bags: 1.0/1.5mt
Storage tips:High purity calcium aluminate cements must be stored in dry conditions, off the ground. In this case, it will retain its proper ties for at least 6 months. In many instances, experience has demonstrated that properties are retained for more than one year.